| PROPERTY | METHOD | UNIT | PP 1064 | PP 1064-1% UV | PP 1064-A | PP 441-E | PP 441 -E(A) | PP 442-F |
|---|---|---|---|---|---|---|---|---|
| Density (23º) | UNE-53-020-73 | g/cm3 | 0,875 - 0,95 | 0,875 - 0,95 | 5810 | 0,92 | 0,92 | 0,92 |
| MFI (230ºC C/2.16 kg) | UNE-EN-ISO 1133:2001 | g/10 min | 8-12 | 8-12 | 9-12 | 6-10 | 10-15 | 1,5-6 |
| Izod Impact Resistance. Notched | UNE-EN-ISO 180 | Kg cm/cm | 7-9 | 15-18 | 5-8 | 5-7 | 6-10 | 15-25 |
| Tensile strength at yield | UNE-EN-ISO 527-1 | Mpa. | 18-28 | 20-35 | 18-30 | 15-30 | 20-30 | 18-30 |
| Elongation at break | UNE-EN-ISO 527-1 | % | 25-100 | 15-100 | 5-20 | 20-150 | 20-100 | 100-300 |
| Elastic Modulus in Tension | UNE-EN-ISO 527-1 | Mpa. | 1200-4000 | 800-1500 | 1000-4000 | 700-1600 | 500-1500 | 800-1500 |
| Elastic Modulus in Flexure | UNE-EN-ISO 178:1993 | Mpa. | 800-1200 | 650-750 | 650-900 | 500-1000 | 800-1250 | 800-1200 |
| Yield strength | UNE-EN-ISO 527-1 | Mpa. | 18-28 | 18-22 | 18-30 | 15-25 | 20-30 | 18-30 |
| Ashes | UNE-EN-ISO 3451-1:1997 | % | 3 | 5 | 6 | 3 | 0-10 | 5 |