| PROPERTY | METHOD | UNIT | PE-LD 321 | PE-LD 322-F | PE-LD 322-F EVA | PE.LD 322-F G-0,3 | PE-LD 322-F LINEAL | PF-LD 322-T | |
|---|---|---|---|---|---|---|---|---|---|
| PHISICAL | Density (23º) | UNE-53-020-73 | g/cm3 | 0,92 | 0,923 | 0,923 | 0,9-0,923 | 0,918-0,923 | 0,923 |
| RHEOLOGICAL | MFI (230ºC C/2.16 kg) | UNE-EN-ISO 1133:2001 | g/10 min | 2-8 | 0,6-0,9 | 0,3-4 | 0,2-0,4 | 1-2,5 | 0,2-0,5 |
| MECHANICAL | Izod Impact Resistance. Notched | UNE-EN-ISO 180 | Kg cm/cm | ||||||
| Tensile strength at yield | UNE-EN-ISO 527-1 | Mpa. | 10-20 | 10-20 | |||||
| Elongation at break | UNE-EN-ISO 527-1 | % | 50-180 | 0-500 | |||||
| Elastic Modulus in Tension | UNE-EN-ISO 527-1 | Mpa. | 1200-1800 | 20-30 | |||||
| Elastic Modulus in Flexure | UNE-EN-ISO 178:1993 | Mpa. | 300-900 | 200-300 | |||||
| Yield strength | UNE-EN-ISO 527-1 | Mpa. | 5-15 | 10-20 | |||||
| VARIOUS | Ashes | UNE-EN-ISO 3451-1:1997 | % | <3 | <3 | <3 | <3 | <3 | <3 |